Substrate-Induced Liquid Layering: A New Insight into the Heterogeneous Nucleation of Liquid Metals

Download (4.1 MB)
journal contribution
posted on 25.07.2019, 13:14 by Sida Ma, Rui Yan, Tao Jing, Hongbiao Dong
Liquid layering, which is a general phenomenon adjacent to the solid substrates, is less understood for its role in heterogeneous nucleation. In this work, the structural features and dynamics of the liquid Al layers induced by the (0001) sapphire and the (0001) TiB2 substrates, respectively, are quantitatively compared based on the ab initio molecular dynamics simulations. An almost fully ordered liquid Al layer is observed adjacent to the TiB2 substrate above the Al melting point, while the liquid layers near the sapphire substrate are weakly ordered with virtually no in-plane translational symmetry. Further liquid layering is facilitated by the ordered liquid layer near the TiB2 substrate, while impeded by the low in-plane ordering of the liquid layers near the sapphire substrate, resulting in different nucleation behaviors for the two systems. The difference in the liquid layering is caused, in part, by the lower adsorption strength at the sapphire–liquid Al interface than that at the TiB2–liquid Al interface. Additionally, the compressive stress imposed on the liquid layers seriously hinders the sapphire-induced liquid layering. We conclude from this work that the interfacial adsorption strength and mismatch alter the heterogeneous nucleation by influencing the features of the substrate-induced liquid layering.

Funding

This research was funded by the National Natural Science Foundation of China, grant number [51320105003] and [51674153], and the Chinese Scholarship Council (CSC). This research used the ALICE High Performance Computing Facility at the University of Leicester. The authors acknowledge the support from the Diamond Light Source for the provision of beam time and the National Laboratory for Information Science and Technology at Tsinghua University for access to supercomputing facilities.

History

Citation

Metals, 2018, 8(7), 521

Author affiliation

/Organisation/COLLEGE OF SCIENCE AND ENGINEERING/Department of Engineering

Version

VoR (Version of Record)

Published in

Metals

Publisher

MDPI

issn

2075-4701

Acceptance date

29/06/2018

Copyright date

2018

Available date

25/07/2019

Publisher version

https://www.mdpi.com/2075-4701/8/7/521

Language

en